Self-adhering Films

Folex Digiprint-IG/WOSC

Specially coated static cling film for Electro Ink with a white glossy surface. The film is heat stabilized for good flatness properties and the coating offers excellent ink transfer and bonding for consistent image performance. The film has a silicon release liner which is removed when applying to a window type surface.

Cut sheets

Art. NumberWidth (mm)FormatLength (mm)Nominal thickness (mm)Packing quantity
06899.250.84400320SRA34500.275100PDF
06899.250.869005007000.275100PDF

Technical data

Characteristic

  • Back layer clings to smooth surfaces (glass, metall) without adhesives, easy to remove
  • Superb ink adhesion and image transfer
  • Easy storage
  • Excellent dimensional stability
  • Suitable for short and long runs
  • Officially approved by HP Indigo test centre
  • Tear resistant
  • Consistent performance
  • Dedicated coating for Indigo Electro Ink
  • No limited shelf life
  • Splash resistant

Finish

  • White glossy

Specifications

Coating PrintsideHP Indigo Electro Ink
Coating Thickness (mil)0.48
Coating Thickness (mm)0.010
Width (inch)12.6
Width (mm)320
PrintsideSpecial reactive coating for toner, glossy side
FormatSRA3
Length (inch)17.72
Length (mm)450
Nominal thickness (mil)11
Nominal thickness (mm)0.275
BacksidePVC Cling layer with thin protection sheet
Total Thickness (mil)11.48
Total Thickness (mm)0.287
Base MaterialPolyester / PVC Film
Packing quantity 100

Compatibility

  • Suitable for Digital Presses from HP Indigo
  • Not compatible with dry toner Digital Presses. (See Folex Digiprint-XE and -NX series).

Handling

  • A preconditioning period of 24 hours within the printing environment is recommended.
  • Please carefully follow the handling instructions supplied with this product as well as the press manufacturers manual.
  • No special handling required.
  • Avoid fingerprints on printing side.

Storage

  • Shelf life: 1 year after delivery
  • Store in the closed original packaging in a cool and dry place at a room temperature of 15 - 25°C and at a humidity of 30 - 60%.